I-UHP 450mm Furnace Graphite Electrodes With Nipples T4L T4N 4TPI
Ipharamitha Yezobuchwepheshe
| Ipharamitha | Ingxenye | Iyunithi | Idatha ye-UHP 450mm(18”). |
| Ububanzi Okuzisholo | I-Electrode | mm(intshi) | 450(18) |
| I-Max Diameter | mm | 460 | |
| Ububanzi obuncane | mm | 454 | |
| Ubude Begama | mm | 1800/2400 | |
| Ubude obukhulu | mm | 1900/2500 | |
| Ubude obuncane | mm | 1700/2300 | |
| Ukuminyana Kwamanje Okuphezulu | KA/cm2 | 19-27 | |
| Ikhono Lamanje Lokuthwala | A | 32000-45000 | |
| Ukumelana Okuqondile | I-Electrode | μΩm | 4.8-5.8 |
| Ingono | 3.4-3.8 | ||
| Amandla e-Flexural | I-Electrode | Mpa | ≥12.0 |
| Ingono | ≥22.0 | ||
| I-Modulus Encane | I-Electrode | I-Gpa | ≤13.0 |
| Ingono | ≤18.0 | ||
| Ukuminyana kwenqwaba | I-Electrode | g/cm3 | 1.68-1.72 |
| Ingono | 1.78-1.84 | ||
| I-CTE | I-Electrode | ×10-6/℃ | ≤1.2 |
| Ingono | ≤1.0 | ||
| Okuqukethwe Umlotha | I-Electrode | % | ≤0.2 |
| Ingono | ≤0.2 |
QAPHELA: Noma yiziphi izimfuneko ezithile kubukhulu zinganikezwa.
Izinhlelo zokusebenza
Ama-electrode e-graphite anamandla aphezulu kakhulu (UHP) asetshenziswa ezinhlelweni ze-Electric Arc Furnace akhiqiza insimbi yekhwalithi ephezulu nezinye izinsimbi. Futhi zisetshenziswa kabanzi ezimbonini ezihlukahlukene, okuhlanganisa amandla enuzi, insimbi, amakhemikhali, nokunye.I-UHP Graphite Electrode yaziwa ngamandla ayo aphezulu emishini kanye nokunemba komshini. Lokhu kuqinisekisa ukuthi ama-electrode e-graphite aqine ngokwanele ukuze amelane namandla amakhulu nezingcindezi ngaphakathi kwesithando somlilo, kuyilapho egcina isimo nobukhulu bawo. I-Gufan izinikele ekukhiqizeni uhla olubanzi lwe-electrode ye-graphite ye-UHP ukuze ihlangabezane nemfuneko yokusebenza kahle okuphakeme kanye nezindleko eziphansi zawo wonke amakhasimende omhlaba.
Ishadi Lenqubo Yokukhiqiza
Sithumele i-imeyili yombuzo, sizokuthinta uma sithola i-imeyili yakho, noma ungithinte kuhlelo lokusebenza lokuxoxa.
Yebo, siyakwenza. Uphawu lokuthumela lungaklanywa futhi luphrintwe njengemfuneko yakho.
Ngokuvamile isikhathi sokulethwa siyizinsuku eziyi-10 kuya kweziyi-15 ngemuva kokukhokha noma ukusayina inkontileka. Noma isikhathi sokulethwa singaxoxisana ngaso uma udinga ukuletha nyanga zonke noma esinye isikhathi esikhethekile.
Imikhiqizo ehlobene
-
Ama-Graphite Electrodes Anezingono Abakhiqizi ...
Iyunithi Yepharamitha Yepharamitha Yobuchwepheshe Iyunithi HP 300mm(12”) Idatha Nominal Diameter Electrode mm(intshi) 300(12) Max Ububanzi mm 307 Min Ububanzi mm 302 Ubude Begama mm 1600/1800 Max Ubude mm 1700/1900 Min Ubude mm10 700 Yamanje Ukuminyana KA/cm2 17-24 Ikhono Lamanje Lokuthwala A 13000-17500 I-Electrode Yokumelana Okuqondile μΩm 5.2-6.5 Nipple 3.5-4.5 Flexu...
-
I-Graphite Electrodes Isebenzisa Ukwenza Insimbi Nge-Nippl...
Iyunithi Yepharamitha Yepharamitha Yezobuchwepheshe RP 500mm(20”) Idatha Ububanzi Begama I-Electrode mm(intshi) 500 Max Ububanzi mm 511 Min Ububanzi mm 505 Ubude Begama mm 1800/2400 Ubukhulu Ubude mm 1900/2500 Min Ubude Ubukhulu mm 1700/230 Ubukhulu Bamanje KA-Kamanje /cm2 13-16 Yamanje I-Capacity A 25000-32000 Specific Resistance Electrode μΩm 7.5-8.5 Nipple 5.8-6.5 Flexur...
-
Ama-Graphite Electrodes Okwenza Insimbi Yamandla Aphakeme...
Iyunithi Yepharamitha Yepharamitha Yezobuchwepheshe HP 400mm(16”) Idatha Ububanzi Begama I-Electrode mm(intshi) 400 Max Ububanzi mm 409 Min Ububanzi mm 403 Ubude Begama mm 1600/1800 Max Ubude mm 1700/1900 Min Ubude mm 1500/170 Ubukhulu bamanje KA-KA cm2 16-24 Yamanje I-Capacity A 21000-31000 Specific Resistance Electrode μΩm 5.2-6.5 Nipple 3.5-4.5 Flexural S...
-
Small Diameter Graphite Electrodes Rod For Elec...
Ishadi Lohlaka Lobuchwepheshe Loku-1:Ipharamitha Yobuchwepheshe Yobubanzi Obuncane I-Graphite Electrode Ingxenye Ukumelana Amandla Aguquguqukayo Amandla Asemusha I-Modulus Ukuminyana CTE I-Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.9℃ ≉ 1.55-1.64 ≤2.4 ≤0.3 Ingono 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≤45.0 ≤45.0 ≤49.0. ≤2.4 ≤0.3 Nip...
-
I-Regular Power Small Diameter Graphite Electrode...
Ishadi Lohlaka Lobuchwepheshe Loku-1:Ipharamitha Yobuchwepheshe Yobubanzi Obuncane I-Graphite Electrode Ingxenye Ukumelana Amandla Aguquguqukayo Amandla Asemusha I-Modulus Ukuminyana CTE I-Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.9℃ ≉ 1.55-1.64 ≤2.4 ≤0.3 Ingono 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≤45.0 ≤45.0 ≤49.0. ≤2.4 ≤0.3 Ni...
-
I-High Purity Sic Silicon Carbide Crucible Graphi...
I-Silicon Carbide Crucible Performance Ipharamitha Yepharamitha Idatha Yepharamitha Yedatha SiC ≥85% Amandla Okuchotshozwa Abandayo ≥100MPa SiO₂ ≤10% I-Porosity Ebonakalayo ≤%18 Fe₂O₃ <1% Ukumelana Nezinga lokushisa ≥1200° I-Bulk Density6° ingakwazi khiqiza ngokwezidingo zamakhasimende Incazelo Okuhamba phambili kwe-thermal---Inokushisa okuhle kakhulu...