Ama-Graphite Electrodes Asebenzisa Ukwenza Insimbi Ngezingono RP HP UHP20 Inch
Ipharamitha Yezobuchwepheshe
| Ipharamitha | Ingxenye | Iyunithi | RP 500mm(20”) Idatha |
| Ububanzi Okuzisholo | I-Electrode | mm(intshi) | 500 |
| I-Max Diameter | mm | 511 | |
| Ububanzi obuncane | mm | 505 | |
| Ubude Begama | mm | 1800/2400 | |
| Ubude obukhulu | mm | 1900/2500 | |
| Ubude obuncane | mm | 1700/2300 | |
| Ukuminyana Kwamanje Okuphezulu | KA/cm2 | 13-16 | |
| Ikhono Lamanje Lokuthwala | A | 25000-32000 | |
| Ukumelana Okuqondile | I-Electrode | μΩm | 7.5-8.5 |
| Ingono | 5.8-6.5 | ||
| Amandla e-Flexural | I-Electrode | Mpa | ≥8.5 |
| Ingono | ≥16.0 | ||
| I-Modulus Encane | I-Electrode | I-Gpa | ≤9.3 |
| Ingono | ≤13.0 | ||
| Ukuminyana kwenqwaba | I-Electrode | g/cm3 | 1.55-1.64 |
| Ingono | ≥1.74 | ||
| I-CTE | I-Electrode | ×10-6/℃ | ≤2.4 |
| Ingono | ≤2.0 | ||
| Okuqukethwe Umlotha | I-Electrode | % | ≤0.3 |
| Ingono | ≤0.3 |
QAPHELA: Noma yiziphi izimfuneko ezithile kubukhulu zinganikezwa.
I-RP Graphite Electrode Advantage
- Umthamo ophezulu wamanje wokuthwala.
- Ukumelana okuphezulu ne-oxidation kanye nokushaqeka kwe-thermal.
- Ukumelana okuvelele kokuqhekeka.
- Ukuzinza kobukhulu obuhle, akulula ukukonakalisa.
- Ukunemba okuphezulu kwemishini, ukuqedwa okuhle kwendawo.
- Amandla aphezulu emishini, ukumelana nogesi okuphansi.
I-RP Graphite Electrode Production Process
Ngokuvamile idinga izinsuku ezingu-20- izinsuku ezingu-45 ngemva kokuthola idiphozi.
Sigcwele emacaleni/amaphalethi okhuni anemicu yensimbi, noma ngokwezidingo zakho.
Sithumele i-imeyili yombuzo, sizokuthinta uma sithola i-imeyili yakho, noma ungithinte kuhlelo lokusebenza lokuxoxa.
Ama-electrode e-Gufan Carbon graphite anezinzuzo zokungabekezeleli okuphansi, amandla aphezulu kagesi kanye ne-thermal, ukumelana okuhle kwe-oxidation, ukumelana nokushaqeka okuhle kokushisa, amandla aphezulu emishini. Singahlinzeka ngemikhiqizo ebanzi ukusuka ku-diamater 200mm kuya ku-700mm ububanzi, okuhlanganisa i-UHP, HP, i-RP grade graphite electrode. Futhi sihlinzeka ngesevisi ye-OEM ne-ODM ukuze kwanelise wonke amakhasimende.
Imikhiqizo ehlobene
-
Ama-Electrode Ekhabhoni Ye-Graphite Ye-Electr Engaphansi...
Iyunithi Yepharamitha Yepharamitha Yezobuchwepheshe RP 350mm(14”) Idatha I-Nominal Diameter Electrode(E) mm(intshi) 350(14) Max Ububanzi mm 358 Min Ububanzi mm 352 Ubude Bebizo mm 1600/1800 Max Ubude mm 1700/1900 Min Ubude 00 mm 1 /1700 Max Ukuminyana Kwamanje KA/cm2 14-18 Ikhono Lamanje Lokuthwala A 13500-18000 I-Electrode Ekhethekile Yokumelana (E) μΩm 7.5-8.5 ingono (N) 5.8...
-
I-UHP 500mm Dia 20 Inch Furnace Graphite Electrod...
Ipharamitha Yobuchwepheshe Izakhiwo Nezakhiwo Zamakhemikhali Ze-D500mm(20”) I-Electrode & Nipple Ipharamitha Yengxenye Iyunithi UHP 500mm(20”) Idatha Nominal Diameter Electrode mm(inch) 500 Max Diameter mm 511 Min Diameter mm 505 Nominal Length mm 1800/2400 Max Ubude 1900/2500 Min Ubude mm 1700/2300 Max Ukuminyana Kwamanje KA/cm2 18-27 Ikhono Lamanje Lokuthwala A 38000-55000 Sp...
-
Small Diameter 225mm Furnace Graphite Electrode...
Ishadi Lohlaka Lobuchwepheshe Loku-1:Ipharamitha Yobuchwepheshe Yobubanzi Obuncane I-Graphite Electrode Ingxenye Ukumelana Amandla Aguquguqukayo Amandla Asemusha I-Modulus Ukuminyana CTE I-Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.9℃ ≉ 1.55-1.64 ≤2.4 ≤0.3 Ingono 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≤45.0 ≤45.0 ≤49.0. ≤2.4 ≤0.3 Nip...
-
I-High Purity Sic Silicon Carbide Crucible Graphi...
I-Silicon Carbide Crucible Performance Ipharamitha Yepharamitha Idatha Yepharamitha Yedatha SiC ≥85% Amandla Okuchotshozwa Abandayo ≥100MPa SiO₂ ≤10% I-Porosity Ebonakalayo ≤%18 Fe₂O₃ <1% Ukumelana Nezinga lokushisa ≥1200° I-Bulk Density6° ingakwazi khiqiza ngokwezidingo zamakhasimende Incazelo Okuhamba phambili kwe-thermal---Inokushisa okuhle kakhulu...
-
Small Diameter Graphite Electrodes Rod For Elec...
Ishadi Lohlaka Lobuchwepheshe Loku-1:Ipharamitha Yobuchwepheshe Yobubanzi Obuncane I-Graphite Electrode Ingxenye Ukumelana Amandla Aguquguqukayo Amandla Asemusha I-Modulus Ukuminyana CTE I-Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.9℃ ≉ 1.55-1.64 ≤2.4 ≤0.3 Ingono 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≤45.0 ≤45.0 ≤49.0. ≤2.4 ≤0.3 Nip...
-
I-Chinese UHP Graphite Electrode Producers Furnac...
Ipharamitha Yobuchwepheshe Ingxenye Iyunithi RP 400mm(16”) Idatha Ububanzi Begama I-Electrode mm(intshi) 400 Max Ububanzi mm 409 Min Ububanzi mm 403 Ubude Begama mm 1600/1800 Ubukhulu Ubude mm 1700/1900 Min Ubude Ubukhulu mm 1500/170 Ubukhulu be-KAmanje /cm2 14-18 Yamanje I-Capacity A 18000-23500 Specific Resistance Electrode μΩm 7.5-8.5 Nipple 5.8-6.5 Flexur...